Export great p355gh material equivalent to Australia

EN-BOILER Steel provides high-quality boiler steel to many natural gas.
Oil and petrochemical companies and is well-known worldwide.

Export great p355gh material equivalent to Australia

Pageviews:

Hot rolling and cold rolling are all the processes of forming steel plates or profiles, which have a great influence on the structure and properties of steel. The rolling of steel is mainly hot rolling, and cold rolling is usually used to produce small size steel and thin plate. With the development of new technologies such as the precision of hot rolling size, shape and surface quality and the continuous emergence of new products, P355GH material equivalent, hot rolled steel strip and steel plate are widely used and have more and more competitive strength in the market.

How to distinguish the inferior steel plate? 1. The surface of the fake and inferior steel plate is easy to produce scab. 2. The material of fake and inferior steel plate is not uniform and there are many impurities. The surface of fake and inferior steel plate is often pitted. Pitting is an irregular and uneven defect on the surface of p355gh material equivalent, steel plate caused by serious wear of rolling groove. Due to the pursuit of profit by the manufacturers of fake and inferior steel plates, the groove rolling often exceeds the standard.

p355gh material equivalent, SA387Gr11CL2 steel chemical composition(%): C: ≤0.15, Si: 0.44—0.86, Mn: 0.35—0.73, P: ≤0.10, S: ≤0.007, Cr: 0.94—1.56, Mo: 0.40—0.70, Ni: ≤0.25, Cu: ≤0.20, Sb: ≤0.0030, Sn: ≤0.015, As: ≤0.016.SA387Gr11CL2 steel mechanical properties: Tensile strength, ksi [MPa]: 75 to 100 [515 to 690]; Yield strength, min, ksi [MPa]: 43 [310]Elongation in 8 in. [200mm], min %: 18; Elongation in 2 in. [50mm], min, %: 22

In October, the demand for finished products improved significantly, breaking through the high of 4.4 million tons per week, and the price of black products went up overall. Among them, coke performed particularly well under the stimulus of downstream shortages and high molten iron output. It wasn't until early November that coke futures prices fell from a high level due to high disk premiums. After six rounds of increases, the spot price also began to weaken. Downstream steel mills were more resistant to the seventh round of increases.

Previous:UAE p355gh material properties inventory Next:How to avoid quality problems of p355gh