Export great p355gh vs p355nh to South Africa

Pageviews:

15CrMo alloy plate is a heat-resistant steel with pearlite structure, which has high thermal strength (δb≥440MPa) and oxidation resistance at high temperatures, and has a certain resistance to hydrogen corrosion. Due to the high content of Cr, C and other alloying elements in steel, the hardening tendency of P355GH vs p355nh and 15CrMo alloy plate is obvious and the weldability is poor. After welding, local high temperature tempering treatment should be carried out. The heat treatment process of 15CrMo alloy plate is as follows: the temperature rise rate is 200°C/h, the temperature is raised to 715°C for 1 hour and 15 minutes, the temperature drop rate is 100°C/h, and the temperature is reduced to 300°C before air cooling.In production and operation, the company always attaches great importance to product p355gh vs p355nh quality. Product quality is stable, performance index is superior, after-sales service is in place, the company's products have been exported to the United States, Southeast Asia, Africa, the Middle East and other countries and regions, occupying a large part of the overseas market p355gh vs p355nh. And a large number of famous enterprises at home and abroad have formed a solid strategic partnership with the company.The heat treatment process can significantly improve the physical properties of steel, improve the compressive strength, ductility and service life of parts, and improve the hardness and wear resistance. Therefore, critical equipment parts and special tools must be quenched and tempered. The quenching and tempering treatment can also improve the production and processing performance of the p355gh vs p355nh product workpiece, thereby improving the production efficiency and production processing quality.Alloying agents like carbon and manganese along with steel lends a malleable nature to A572 structural high tensile steel plates, p355gh vs p355nh, letting them be formed into various structurals that adapt quickly to constantly evolving needs of an edifice, thereby being flexible to changes. High tensile steel plates facilitate an increased load bearing capacity; their lighter bodies handle the extra weight without giving in to pressures. Heavy lifting and moving vehicles built from them increase weight bearing capacity, reduce time and labour cost to increase profits.The after-sale service of iron and steel products includes after-sale tracking service, technical guidance, transfer of relevant bills, handling of objections and many other contents. The handling of quality objections accounts for a large proportion. When dealing with these problems, we should distinguish the responsibilities, and compensate or return the inconvenience or loss caused to users due to steel.