The chemical composition and mechanical properties requirements on 16mo3 material properties
EN-BOILER Steel provides high-quality boiler steel to many natural gas.
Oil and petrochemical companies and is well-known worldwide.
The chemical composition and mechanical properties requirements on 16mo3 material properties
Pageviews:
What are the characteristics of medium and thick plate, 16Mo3 material properties? First, the performance of shock resistance and vibration is very good, so the application of medium and thick plates in buildings and bridges can greatly improve the safety. Second, the bearing capacity of medium and thick plate, 16mo3 material properties is good, the performance is excellent. The bridge, the automobile girder steel plate, and buildings have strict load-bearing requirements, and it is easy to cause accidents if the steel materials not meet the requirements, so the selection of steel is more stringent.
High quality steel sheet and plate product 16mo3 material properties supply 10.5*1970*7950, 13*1300*4350, 11*1900*12500, 12.5*2870*7100, 11*1870*12500, 10.5*1970*8000, 13*1520*7950, 11*1910*9000, 12.5*2900*8250, 11*1870*13500, 10.5*2350*6200, 14*1440*6100, 11*3100*10000, 13*1510*4850, 11*1870*9300, 11*1570*12000, 14*1800*9750, 11.5*2640*7600, 13*2380*6000, 11*2400*10000.
The hot rolling method is to heat the 16mo3 material properties steel material to about 1000 ℃ ~ 1250 ℃ and use the rolling mill to roll it. The traditional hot rolling process is generally divided into the following two steps: the first step is to use the primary rolling mill or billet rolling mill to roll the ingot, billet or continuous casting billet into a certain shape and size of billet. This kind of 16mo3 material properties rolling process is usually called semi-finished product production, also called blank production.
16mo3 material properties controlled rolling is that, on the basis of adjusting the chemical composition of 16mo3 material properties, by controlling the heating temperature, rolling temperature, deformation system and other process parameters, the change law of austenite structure and the microstructure of phase transformation products are controlled, so as to achieve the purpose of refining the structure and improving the strength and toughness of 16mo3 material properties.