What is the manufacturing method of p355gh material equivalent

Pageviews:

In recent years, in line with the development trend of iron and P355GH material equivalent steel industry at home and abroad, we have accelerated the transformation of development mode, promoted structural adjustment, and formed a rich product series of medium and thick plates, hot rolled steel coils, profiles, steel pipes, etc., which p355gh material equivalent are widely used in automobiles, long-span bridges, railways, machinery, ocean and so on fields. Meanwhile, we also provide deep processing for the steel materials.

Wear resistant steel plate p355gh material equivalent is an important material for industrial application. The traditional wear resistant steel is the high manganese steel which hardens under the impact load. The premise of its function must be subjected to enough impact load. With the development of wear resistant steel technology, NM series steel plate breaks through the limitation of traditional high manganese steel and realizes the application space of wear-resistant steel. The main p355gh material equivalent grades of NM series wear resistant steel plates are NM360, NM400, NM450, NM500, NM550, NM600.

Grade E, Grade EH32, Grade EH36 series shipbuilding steel products have good comprehensive mechanical properties, welding performance, process performance. Our shipbuilding steel plate and p355gh material equivalent steel sections are suitable for manufacturing structural parts such as ship hull structures, docks, oil production platforms, marine transmission pipelines, coastal power plants, wharf facilities in ocean, coastal and inland navigation areas.

The common delivery status of p355gh material equivalent, SA516 Gr 70 plate is as follows: 1) SA516 Gr 70 plate quenching: the process of rapid cooling after heating to the temperature above the phase transformation point. 2) SA516 Gr 70 plate normalizing: after heating above the phase transition temperature, it is cooled normally (in air). 3) SA516 Gr 70 plate annealing: heating to above the phase transition temperature, cooling slowly. 4) SA516 Gr 70 plate tempering: after quenching, it is heated to a certain temperature (lower than the quenching temperature), kept warm, and then cooled.

p355gh material equivalent, Q345B steel plate strength has much to do with its thickness. First, the min. yield strength of Q345B steel plate: 345 Mpa for thickness ≤16mm, 335 Mpa for thickness 16-40mm, 325 Mpa for thickness 40-63mm, 315 Mpa for thickness 63-80mm, 305 Mpa for thickness 80-100mm, 285 Mpa for thickness 100-150mm, 275 Mpa for thickness 150-200mm, 265 Mpa for thickness 200-250mm. Second, the tensile strength of Q345B steel plate: 470-630 Mpa for thickness ≤100mm, 450-600 Mpa for thickness 100-250mm.

It is a modern high-tech professional enterprise integrating scientific research, p355gh material equivalent production and sales. The company is mainly engaged in the manufacture, installation and commissioning of boiler and pressure vessel, chemical, metallurgical, petroleum and other equipment, as well as p355gh material equivalent process technology development, technology transfer and related technical consulting and technical services.

There is a careful, patient, enthusiastic and thoughtful after-sales team, a professional distribution, ultra-efficient warehouse and logistics center, a marketing team with marketing expertise, an innovative technology center with strong steel technology, an experienced manufacturing center with rigorous professionalism Quality Inspection Center, an operation team with many years of administrative management experience. Such a strong combination of teams makes BEBON a steel giant in Henan Province.