1/6 inch thickness p295gh steel used for petroleum

Pageviews:

In recent years, in line with the development trend of iron and P295GH steel used for petroleum steel industry at home and abroad, we have accelerated the transformation of development mode, promoted structural adjustment, and formed a rich product series of medium and thick plates, hot rolled steel coils, profiles, steel pipes, etc., which p295gh steel used for petroleum are widely used in automobiles, long-span bridges, railways, machinery, ocean and so on fields. Meanwhile, we also provide deep processing for the steel materials.

The hardness value of NM600 wear-resistant steel plate reaches 600 HBW, and it is generally used in extremely severe wear occasions, and mainly used to replace cast steel, chromium alloy cast iron and surface hardening metal p295gh steel used for petroleum. Although the hardness of NM600 wear-resistant steel plate is very high, we can machine, weld and cut it. Although the hardness of NM600 wear-resistant steel plate is very high, it still has high impact toughness.

The mechanical properties of 20MnV steel are as follows: tensile strength 785 MPa, yield strength 590 MPa, elongation after fracture 10%, reduction of area 40%, impact absorption energy 55 J. p295gh steel used for petroleum, 20MnV steel has good properties, good strength, toughness and plasticity, good hardenability and machinability. After carburizing, 20MnV steel can be directly quenched without secondary quenching to improve the core structure. The weldability of 20MnV steel is good, but there is temper brittleness at 300-360 ℃ during heat treatment.

Cold rolled p295gh steel used for petroleum steel sheet can be produced by two high mill, four high reversing mill, multi high reversing mill and tandem cold mill. Although there are still only two work rolls in four high and multi high rolling mills, each work roll is supported by one or more large diameter backup rolls, which can prevent deflection of work roll. As a result, wide and thinner p295gh steel used for petroleum steel plates can be produced. For example, 20 high mill can produce as thin as 0. 001 mm sheet, but the two high mill can only produce as thin as 0. 35mm sheet

Chemical composition of Q420 steel: C ≤ 0.20, Si ≤ 0.50, Mn ≤ 1.70, P ≤ 0.035, S ≤ 0.035, Nb ≤ 0.07, V ≤ 0.20, Ti ≤ 0.20, Cr ≤ 0.30, Ni ≤ 0.80, Cu ≤ 0.30, N ≤ 0.015, Mo ≤ 0.20. The mechanical properties of Q420 steel are: yield strength ≥ 340 MPa, tensile strength 500-680 MPa, elongation after fracture ≥ 18%, impact energy 34J. p295gh steel used for petroleum, Q420 steel has good mechanical properties and weldability, good cold and hot workability. Q420 steel is mainly used for manufacturing mining machinery, heavy vehicles, ships, bridges, medium and high pressure boilers, vessels and other large welding and structural parts.

After sales service support personnel pay attention to commitment in their work. In the process of people to people communication, mutual trust is an important factor for the long-term and stable communication. After sales service personnel must do what they say in the process of communication with customers.